LENETA WC-55 Film Applicator film thickness 106µm
LENETAWC-55 Lacquer Film Applicator Wire diameter 1.40mm, WC-55 Lacquer Film Applicator is made of all stainless steel
Model：
WC-55
LENETA WC-55 Mayer RodsSPEC
LENETA WC-55 Mayer RodsDetails
LENETA WC-55 Mayer RodsPacking list
- SKU
- NB010387
- Production process
- Wire-wound
- WFT
- 106µm
- diameter
- 12.7mm
- Total length
- 305mm
- Wire diameter
- 1.40mm
- Application width
- 254mm
- grip width
- 25+25mm
- material
- stainless steel
WC-55
Mayer Rods
Wire bar applicator
The coating is prepared into a film of a certain thickness, also known as a wire rod applicator, Meyer rod, and winding rod.
Features
Wire Diameter: 0.064~1.9mm(2.5~75mils)
Prepared coating film thickness: 4.5~150μm (0.18~6mils)
Coating Width: 254mm (10inches) long enough to meet most standard size baseplates and cardboards.
Bar length: 305mm (12inches). There are 25mm long grip parts at each end.
Bar diameter: 12.7mm (1/2inch). Thick enough to provide basic good rigidity.
Material: All stainless steel. Even water-based paints do not rust or corrode. Non-magnetic, allowing for use with steel plates on magnetic cards.
Parameters
| Model | Wire diameter | Coating film thickness | Coating width |
| WC-2.5 | 0.064mm(2.5mil) | 4.5µm(0.18 mil) | 254mm(10 in) |
| WC-3 | 0.075mm(3mil) | 5µm(0.2 mil) | 254mm(10 in) |
| WC-4 | 0.10mm(4mil) | 8µm(0.3 mil) | 254mm(10 in) |
| WC-6 | 0.15mm(6mil) | 10µm(0.4 mil) | 254mm(10 in) |
| WC-8 | 0.20mm(8mil) | 13µm(0.5 mil) | 254mm(10 in) |
| WC-10 | 0.25mm(10mil) | 16µm(0.65 mil) | 254mm(10 in) |
| WC-12 | 0.30mm(12mil) | 20µm(0.8 mil) | 254mm(10 in) |
| WC-14 | 0.36mm(14mil) | 24µm(0.95 mil) | 254mm(10 in) |
| WC-16 | 0.41mm(16mil) | 28µm(1.1 mil) | 254mm(10 in) |
| WC-18 | 0.46mm(18mil) | 32µm(1.25 mil) | 254mm(10 in) |
| WC-20 | 0.51mm(20mil) | 35µm(1.4 mil) | 254mm(10 in) |
| WC-22 | 0.56mm(22mil) | 38µm(1.5 mil) | 254mm(10 in) |
| WC-24 | 0.61mm(24mil) | 42µm(1.7 mil) | 254mm(10 in) |
| WC-26 | 0.66mm(26mil) | 47µm( 1.8mil) | 254mm(10 in) |
| WC-28 | 0.71mm(28mil) | 50µm(2.0 mil) | 254mm(10 in) |
| WC-30 | 0.76mm(30mil) | 55µm(2.2 mil) | 254mm(10 in) |
| WC-32 | 0.81mm(32mil) | 59µm(2.3 mil) | 254mm(10 in) |
| WC-34 | 0.86mm(34mil) | 63µm(2.5 mil) | 254mm(10 in) |
| WC-36 | 0.91mm(36mil) | 68µm(2.7 mil) | 254mm(10 in) |
| WC-38 | 0.97mm(38mil) | 72µm(2.8 mil) | 254mm(10 in) |
| WC-40 | 1.02mm(40mil) | 75µm(3.0 mil) | 254mm(10 in) |
| WC-42 | 1.07mm(42mil) | 81µm(3.2 mil) | 254mm(10 in) |
| WC-44 | 1.12mm(44mil) | 85µm(3.3 mil) | 254mm(10 in) |
| WC-46 | 1.17mm(46mil) | 89µm(3.5 mil) | 254mm(10 in) |
| WC-48 | 1.22mm(48mil) | 93µm(3.7 mil) | 254mm(10 in) |
| WC-50 | 1.27mm(50mil) | 98µm(3.8 mil) | 254mm(10 in) |
| WC-52 | 1.32mm(52mil) | 100µm(4.0 mil) | 254mm(10 in) |
| WC-55 | 1.40mm(55mil) | 106µm(4.2 mil) | 254mm(10 in) |
| WC-60 | 1.52mm(60mil) | 114µm(4.5 mil) | 254mm(10 in) |
| WC-65 | 1.65mm(65mil) | 125µm(5.0 mil) | 254mm(10 in) |
| WC-70 | 1.78mm(70mil) | 138µm(5.5 mil) | 254mm(10 in) |
| WC-75 | 1.91mm(75mil) | 150µm(6.0 mil) | 254mm(10 in) |
| WC-212 | N/A | N/A | 254mm(10 in) |
Optional
|
|
|
FAQ
QMeet JB/T5946 Mayer Rods
A
WC-55 Mayer Rods, please refer to it.
QCan silicone coatings be applied to quartz Glass substrates?
A
Yes, choose quartz Glass as the substrate, with Mayer Rods Coating prepared above coated on the surface of the treated quartz Glass substrate, at room temperature to evaporate the solvent into the oven, at a certain temperature curing film formation.
QSolid content of the sample is 32% and Dry-Film is 34 microns. Do you have any suggestions?
A
This one is fine.
Standard